[1]赵晖,朱其柱,金光,等.电流密度对纯铝微弧氧化膜结构及硬度的影响[J].深圳大学学报理工版,2014,31(1):83-87.[doi:10.3724/SP.J.1249.2014.01083]
 Zhao Hui,Zhu Qizhu,Jin Guang,et al.Effect of current density on micro-structure and micro-hardness of micro-arc oxidation coatings on aluminum[J].Journal of Shenzhen University Science and Engineering,2014,31(1):83-87.[doi:10.3724/SP.J.1249.2014.01083]
点击复制

电流密度对纯铝微弧氧化膜结构及硬度的影响()
分享到:

《深圳大学学报理工版》[ISSN:1000-2618/CN:44-1401/N]

卷:
第31卷
期数:
2014年第1期
页码:
83-87
栏目:
材料科学
出版日期:
2014-01-14

文章信息/Info

Title:
Effect of current density on micro-structure and micro-hardness of micro-arc oxidation coatings on aluminum
文章编号:
20140112
作者:
赵晖1朱其柱2金光1杜春燕1杨金花1
1)沈阳理工大学材料科学与工程学院,沈阳 110159
2) 浙江巨科铝业有限公司,浙江台州 318058
Author(s):
Zhao Hui1 Zhu Qizhu2 Jin Guang1 Du Chunyan1 and Yang Jinhua1
1) College of Materials Science and Engineering, Shenyang Ligong University, Shenyang 110159, P.R.China
2) Zhejiang GKO Aluminium Co LTD, Taizhou 318058, Zhejiang Province, P.R.China
关键词:
材料表面防护纯铝微弧氧化电流密度微观形貌显微硬度
Keywords:
material surface protection aluminum micro-arc oxidation current density micro-morphology micro-hardness
分类号:
TG 174.4
DOI:
10.3724/SP.J.1249.2014.01083
文献标志码:
A
摘要:
在恒流模式下,研究纯铝在含有硅酸钠、氟化钾、甘油和氢氧化钾的电解液中的微弧氧化.考察正负电流密度比值恒定时,不同电流密度对陶瓷膜表面形貌、厚度、相组成及显微硬度的影响.结果表明,随电流密度的增大,陶瓷膜表面微孔数量减少,表面微孔孔径和陶瓷膜厚度增大;陶瓷膜主要由α-Al2O3和γ-Al2O3组成,且随电流密度的增大,膜层中α-Al2O3与γ-Al2O3相衍射峰明显增强;陶瓷膜显微硬度随电流密度的增加而增大,显微硬度最高可达27.331 GPa,远高于基体显微硬度的0.687 GPa.
Abstract:
Micro-arc oxidation was carried out on aluminum surface in a solution containing sodium silicate, potassium fluoride, glycerol and potassium hydroxide at a constant applied current density.The influences of different current density on morphology, thickness, phase composition and hardness of micro-arc oxidation (MAO) coatings were investigated when the ratio of anodic current density to cathodic current density was kept unchanged.The results show that with the increase of current density, the number of micro-pores decreases while the size of micro-pores, the thickness and the micro-hardness increase.The MAO coating are mainly composed of α-Al2O3 and γ-Al2O3.The intensity of α-Al2O3 and γ-Al2O3 diffraction peaks increase obviously with the increase of current density.The micro-hardness of MAO coatings can reach 27.331 GPa while that of the substrate is only 0.687 GPa.

参考文献/References:

[1] Liu Jing’an,Xie Shuisheng.The Application and Development of Aluminum Alloy Material [M].Beijing: Metallurgical Industry Press,2011:1-8.(in Chinese)
刘静安,谢水生.铝合金材料应用与开发[M].北京: 冶金工业出版社,2011:1-8.
[2] Jiang Yongfeng,Li Junming, Jiang Bailing, et al.The factor analysis of aluminum alloy micro-arc oxidation ceramic layers [J].Surface Technology,2007,15(3): 309-312.(in Chinese)
蒋永锋,李均明,蒋百灵,等.铝合金微弧氧化陶瓷层形成因素的分析[J].表面技术,2007,15(3):309-312.
[3] Yang Yue, Chen Bin. Effect of SiC nanoparticles on 6060 aluminum alloy micro-arc oxidation film organization structure and corrosion resistance [J].Jourmal of Jilin University,2011,41(51):106-110.(in Chinese)
杨悦,陈彬.SiC纳米颗粒对6060型铝合金微弧氧化膜组织结构及耐蚀性能的影响[J].吉林大学学报,2011,41(51):106-110.
[4] Pan Mingqiang, Chi Guanxin,Wei Dongbo, et al.China’s aluminum/magnesium alloy micro-arc oxidation technology research and application status [J].Materials Protection,2010,4(4): 10-14.(in Chinese)
潘明强,迟关心,韦东波,等.我国铝/镁合金微弧氧化技 术的研究及应用现状[J].材料保护,2010,43(4):10-14.
[5] ZhaoYingpeng, ZhangXiaoyan, GeFei, etal. Themicro-arc oxidation coating wear resistance of cast aluminum alloy under different system[J].Light Metal,2012(2):60-62.(in Chinese)
赵英鹏,张晓燕,葛飞,等.不同体系下铸造铝合金微弧氧化膜层的耐磨性能研究[J].轻金属,2012(2):60-62.
[6] Ma S N,Suo X B,Qiu J.Fabrication of n-SiO2 reinforced Al2O3 composites coatings on 7A52 aluminum alloy by micro-arc oxidation[J].Advanced Materials Research,2010,97/98/99/100/101:1463-1466.
[7] Arslan E,Totik Y,Demirci E E,et al. High temperature wear behavior of aluminum oxide layers produced by AC micro-arcoxidation[J].Surface&CoatingsTechnology, 2009(204):829-833.
[8] Duan Guan,Li Jinfu,Wang Yongjun,et al. Research about aluminum alloy micro-arc oxidation [J].Surface Technology,2007,36(3):30-33.(in Chinese)
段关,李金富,王拥军,等.铝合金的微弧氧化研究[J].表面技术,2007,36(3):30-33.
[9] Pan Mingqiang,Wei Dongbo,Chi Guanxin,et al.The effect of constant current micro-arc oxidation process parameters on film surface roughness[J].Materials Protection,2009,42(7):29-32.(in Chinese)
潘明强,韦东波,迟关心,等.恒流微弧氧化工艺参数对膜层表面粗糙度的影响[J].材料保护,2009,42(7):29-32.
[10] Liu Rongming,Guo Feng,Li Pengfei.The impact of voltage on the formation of aluminum alloy micro-arc oxidation ceramic[J].Transactions of Materials and Heat Treatment,2008,29(1):137-140.(in Chinese)
刘荣明,郭锋,李鹏飞.电压对铝合金微弧氧化陶瓷层形成的影响[J].材料热处理学报,2008,29(1):137-140.
[11] Chen Yanjun,Feng Changjie,Shao Zhisong,et al.The research progress of aluminum alloy micro-arc oxidation technology[J].Materials Review,2010,24(5):132-136.(in Chinese)
陈妍君,冯长杰,邵志松,等.铝合金微弧氧化技术的研究进展[J].材料导报,2010,24(5):132-136.
[12] He Siyu.The Structure and Performance of Aluminum Alloy Micro-arc Oxidation Film [D].Jinan:Shandong University,2012.(in Chinese)
何思宇.铝合金表面微弧氧化膜的组织结构与性[D]. 济南: 山东大学, 2012.
[13] Wang Shuang,Guo Feng,Liu Liang,et al.Effect of process parameters on thickness and morphology of micro-arc oxidation ceramic coating of zirconium alloy [J].Rare Metal Materials and Engineering,2008, 37(80):1466-1470.(in Chinese)
王双,郭锋,刘亮,等.微弧氧化工艺对锆合金表面陶瓷层厚度和形貌的影响[J].稀有金属材料与工程,2008,37(8):1466-1470.
[14] Venugopal A, Panda R, Manwatkar S, et al. Effect of micro arc oxidation treatment on localized corrosion behaviour of AA7075 aluminum alloy in 3.5% NaCl solution [J].Transactions of Nonferrous Metals Society of China,2012,22:700-710.
[15] Zhou Ya,Jiang Yimin,Zhou Jia. The research status of aluminum alloy micro-arc oxidation coating corrosion resistance [J].Failure Analysis and Prevention,2012,7(1):57-62.(in Chinese)
周雅,江溢民,周佳.铝合金微弧氧化膜层耐蚀性研究现状[J].失效分析与预防,2012,7(1):57-62.

备注/Memo

备注/Memo:
Received:2010-06-03;Revised:2013-10-25;Accepted:2013-12-15
Foundation:Liaoning Science and Technology Fund Project (2009222006)
Corresponding author:Professor Zhao Hui. E-mail: zhaohui_1968@sina.com
Citation:Zhao Hui,Zhu Qizhu,Jin Guang,et al. Effect of current density on micro-structure and micro-hardness of micro-arc oxidation coatings on aluminum[J]. Journal of Shenzhen University Science and Engineering, 2014, 31(1): 83-87.(in Chinese)
基金项目:辽宁省科学技术基金资助项目(2009222006)
作者简介:赵晖(1968-),男(汉族),山东省烟台市人,沈阳理工大学教授. E-mail: zhaohui_1968@sina.com
引文:赵晖,朱其柱,金光,等. 电流密度对纯铝微弧氧化膜结构及硬度的影响[J]. 深圳大学学报理工版,2014,31(1):83-87.
更新日期/Last Update: 2014-01-08